  • Effect of stirring time on synthesis of ultra fine α-Al2O3 powder by a simple sol-gel method
  • F. Mirjalilia,*, Luqman Chuahb,d and Hasmaliza Mohamadc
  • a Maybod branch, Islamic Azad University, Maybod, Iran b Department of chemical & Environmental Engineering, Faculty of Engineering, University Putra Malaysia, Malaysia c Schools of Material & Mineral Resources Engineering, University Sains Malaysia, Malaysia d Laboratory of Biopolymers and Bioderivatives, Institute of Tropical Forestry and Forest Products (INTROP), University Putra Malaysia, Malaysia
Abstract
The present paper tends to explore the effect of stirring time on the synthesis of nano α-Al2O3 particles. In this study, alumina nanoparticles were synthesized through an alkoxide route implementing sol-gel method in which aqueous solutions of aluminum isopropoxide and 0.5M aluminum nitrate nanohydrate were used to prepare an alumina sol. Sodium dodecylbenzen sulfonate was used as the surfactant stabilizing agent. The prepared solution was stirred for different times (24, 36, 48 and 60 hours) at 60 oC. The samples were, then, characterized by Brunauer-Emmet-Teller method, X-ray diffraction, thermogravimetry analysis, differential scanning calorimetry, Fourier transform infrared spectrometry , scanning electron microscopy and transmission electron microscopy. The introduction of different stirring times affected the particle size and shape and the degree of aggregation. By increasing the stirring time (starting from 24 to 48 hours), the particle size decreased, but there was a harder agglomeration for the samples with 60 hours stirring time. The finest particle size (20-30 nm) was obtained at 48 hours stirring time.

Keywords: α-Al2O3, X-ray methods, Electron Microscopy

This Article

  • 2011; 12(6): 738-741

    Published on Dec 31, 2011