  • Characterization of Cr-P-C/MoS2 composite plating electro-deposited from trivalent chromium
  • Characterization of Cr-P-C/MoS2 composite plating electro-deposited from trivalent chromium
  • a School of Materials Science and Engineering, Inha University, 100 Inha-ro, Nam-gu, Incheon 22212, Korea b T&C Co., Ltd, 21 Oido-ro, Siheung-si, Gyeonggi-Do 15014, Korea c Metal & Machinery Team, Korea Conformity Laboratories (KCL), 199 Gasan digital 1-ro, Geumcheon-gu, Seoul 08503, Korea
Abstract
Chromium plating is a common surface treatment technique extensively applied in industry due its excellent properties which include substantial hardness, abrasion resistance, corrosion resistance, surface color, and luster. In this study, the effect of MoS2 particles of the composite coating was investigated. To improve the lubrication of mold, Cr-P-C/MoS2 composite plating was studied by varying the MoS2 content. The current efficiency of the composite plating incorporated MoS2 particles was increased at MoS2 contents of 0.5 and 1.0 g/l due to the incorporation of fine particles. On the other hand, when the content of MoS2 is 1.0 g/l or more, the current efficiency is lowered due to an increase in impact on the cathode surface. In order to evaluate the mechanical properties of Scratch test were conducted. Scratch test confirmed the lubricity and abrasion resistance characteristics revealed that the composite plating with added MoS2 had relatively low surface roughness and uniform surface modification to improve its properties.

Keywords: Cr-P-C/MoS2, Composite plating, Electro-deposition, Abrasion resistance, Trivalent chromium

This Article

  • 2018; 19(6): 445-449

    Published on Dec 31, 2018

Correspondence to

  • E-mail: