  • Synthesis and microwave dielectric properties of Li2ZnTi3O8 ceramics by the reaction-sintering process
  • G.G. Yaoa,*
  • a School of Science, Xi'an University of Posts and Telecommunications, Xi'an 710121, China
Abstract
Li2ZnTi3O8 ceramics were prepared by reaction-sintering process (calcination free). The crystal phase and microstructure were investigated using X-ray diffraction (XRD) and scanning electron microscopy (SEM). A pure phase of Li2ZnTi3O8 ceramics sintered at 1075 oC-1150 oC with cubic spinel structure was confirmed by XRD. The microwave dielectric properties (εr, Qxf) of Li2ZnTi3O8 ceramics were strongly dependent on the densification and grain size. The τf of Li2ZnTi3O8 ceramics was almost independent with the sintering temperatures. In particular, Li2ZnTi3O8 ceramics by reaction-sintering method sintered at 1125 oC for 5 hrs exhibited good combination microwave dielectric properties of εr = 21.7, Q × f = 70 500 GHz (at 7.5 GHz) and τf=−13 ppm/oC.

Keywords: reaction-sintering, Li2ZnTi3O8, dielectric properties.

This Article

  • 2015; 16(1): 41-44

    Published on Feb 28, 2015

Correspondence to

  • E-mail: