  • Synthesis of CaSiAlN3 : Eu2+ phosphor by liquid phase precursor method 
  • Deok Su Joa, Karupannan Senthila, Young Hyun Songa, Takaki Masakia and Dae-Ho Yoona,b,*
  • a School of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746, Korea b SKKU Advanced Institute of Nanotechnology (SAINT), Sungkyunkwan University, Suwon 440-746, Korea
Abstract
The synthesis of Ca0.92AlSiN3 : 0.08Eu(2+) (CASN : Eu) phosphor was investigated by a carbothermal reduction and nitridation (CRN) reaction using a liquid-phase precursor (LPP) method. The carbon source for CRN reaction was prepared by a precursor of the LPP method, and carbonization of the precursor was carried out at 300 degrees C. CASN : Eu phosphor was constructed through the CRN reaction at synthesis temperatures of 1500 and 1600 degrees C. The obtained CASN : Eu phosphors were of a mixed powder with AlN. The main emission spectra of the CASN : Eu phosphors were located at 630 nm, and the main excitation spectra were in the range of 370-470 nm.

Keywords: CaSiAlN3: Eu2+; Phosphor; Nitride; LPP; CRN

This Article

  • 2014; 15(4): 259-261

    Published on Aug 31, 2014

Correspondence to

  • E-mail: